Dental composite

Overview
Dental composites, also called white fillings, are a group of restorative materials used in dentistry. As with other composite materials, a dental composite typically consists of a resin-based oligomer matrix, such as a bisphenol A-glycidyl methacrylate BISMA or urethane dimethacrylate (UDMA), and an inorganic filler such as silicon dioxide silica. Compositions vary widely, with proprietary mixes of resins forming the matrix, as well as engineered filler glasses and glass ceramics. The filler gives the composite wear resistance and translucency. A coupling agent such as silane is used to enhance the bond between these two components. An initiator package begins the polymerization reaction of the resins when external energy (light/heat etc.) is applied. A catalyst package can control its speed.

Direct Dental Composites
Direct dental composites can be used for:
 * Filling cavities in teeth, as fillings, inlays and/or onlays
 * Filling gaps (diastemas) between teeth using a shell-like veneer or
 * Minor reshaping of teeth
 * Partial crowns on single teeth

Direct dental composites are placed by the dentist in a clinic setting. Polymerization is accomplished typically with a handheld curing light that emits specific wavelengths keyed to the initiator and catalyst packages involved. When using a curing light, remember that the light should be held as close to the resin surface as possible, a shield should be placed between the light tip and the operator's eyes, and that curing time should be increased for darker resin shades. Light cured resins provide denser restorations than self-cured resins because no mixing is required that might introduce air bubble porosity.

The main advantage of a direct dental composite over traditional materials such as amalgam is improved aesthetics. Composites can be made in a wide range of tooth colours allowing near invisible restoration of teeth. Composites are glued into teeth and this strengthens the tooth's structure. The discovery of acid etching (producing enamel irregularities ranging from 5-30 micrometers in depth) of teeth to allow a micromechanical bond to the tooth allows good adhesion of the restoration to the tooth. This means that unlike silver filling there is no need for the dentist to create retentive features destroying healthy tooth. The acid-etch adhesion prevents microleakage; however, all white fillings will eventually leak slightly. Very high bond strengths to tooth structure, both enamel and dentine, can be achieved with the current generation of dentine bonding agents. The downside to composite when compared to amalgam is a shorter lifespan of the filling, and the high likelihood of requiring root canal therapy if the failure of the filling is not caught quickly. Amalgam fillings may crack a portion of the tooth off, but otherwise tend to fail at a much slower rate.

Initially, composite restorations in dentistry were very prone to leakage and breakage due to weak compressive strength. In the 1990s and 2000s, composites were greatly improved and are said to have a compression strength sufficient for use in posterior teeth. Today's composite resins have low polymerization shrinkage and low coefficients of thermal shrinkage, which allows them to be placed in bulk while maintaining good adaptation to cavity walls. The placement of composite requires meticulous attention to procedure or it may fail prematurely. The tooth must be kept perfectly dry during placement or the resin will likely fail to adhere to the tooth. Composites are placed while still in a soft, dough-like state, but when exposed to light of a certain blue wavelength, they polymerize and harden into the solid filling. It is challenging to harden all of the composite, since the light often does not penetrate more than 2-3 mm into the composite. If too thick an amount of composite is placed in the tooth, the composite will remain partially soft, and this soft unpolymerized composite could ultimately irritate or kill the tooth's nerve. A good dentist will place a deep filling in numerous increments, curing each 2-3 mm section fully before adding the next. In addition, the clinician must be careful to adjust the bite of the composite filling, which can be tricky to do. If the filling is too high, even by a subtle amount, that could lead to chewing sensitivity on the tooth. A properly placed composite is comfortable, aesthetically pleasing, strong and durable, and could last 10 years or more. (By most North American insurance companies 2 years minimum)

The most desirable finish surface for a composite resin can be provided by aluminum oxide disks. Classically, Class III composite preparations were required to have retention points placed entirely in dentin. A syringe was used for placing composite resin because the possibility of trapping air in a restoration was minimized. Modern techniques vary, but conventional wisdom states that because there have been great increases in bonding strength due to the use of dentin primers in the late 1990s, physical retention is not needed except for the most extreme of cases. Primers allow the dentin's collagen fibers to be "sandwiched" into the resin, resulting in a superior physical and chemical bond of the filling to the tooth. Indeed, composite usage was highly controversial in the dental field until primer technology was standardized in the mid to late 1990s. The enamel margin of a composite resin preparation should be beveled in order to improve aesthetics and expose the ends of the enamel rods for acid attack. The correct technique of enamel etching prior to placement of a composite resin restoration includes etching with 30%-50% phosphoric acid and rinsing thoroughly with water and drying with air only. In preparing a cavity for restoration with composite resin combined with an acid etch technique, all enamel cavosurface angles should be obtuse angles. Contraindications for composite include varnish and zinc oxide-eugenol. Composite resins for Class IIs were not indicated because of excessive occlusal wear in the 1980s and early 1990s. Modern bonding techniques and the increasing unpopularity of amalgam filling material have made composites more attractive for Class II restorations. Opinions vary, but composite is regarded as having adequate longevity and wear characteristics to be used for permanent Class II restorations (although amalgam has proved to last considerably longer and have reduced leakage and sensitivity when compared to Class II composite restorations).

Indirect Dental Composites
Indirect dental composites can be used for:
 * Filling cavities in teeth, as fillings, inlays and/or onlays
 * Filling gaps (diastemas) between teeth using a shell-like veneer or
 * Reshaping of teeth
 * Full or partial crowns on single teeth
 * And even bridges spanning 2-3 teeth

This type of composite is cured outside the mouth, in a processing unit that is capable of delivering higher intensities and levels of energy than handheld lights can. Indirect composites can have higher filler levels, and are cured for longer times. As a result, they have higher levels and depths of cure than direct composites. For example, an entire crown can be cured in a single process cycle in an extra-oral curing unit, compared to a millimeter layer of a filling.

As a result, full crowns and even bridges (replacing multiple teeth) can be fabricated with these systems. A stronger, tougher and more durable product is likely.